Tipo do documento: Dissertação
Título: Análise da permeabilidade dentinária após irradiação com o laser de nd:yag associado a adesivo universal e diferentes biovidros.
Título(s) alternativo(s): Analysis of dentin permeability after irradiation with the nd: yag laser associated with universal adhesive and different bioglass.
Autor: PENHA, Karla Janilee De Souza 
Primeiro orientador: FIROOZMAND, Leily Macedo
Primeiro membro da banca: BAUER, José Roberto de Oliveira
Segundo membro da banca: TAVAREZ, Rudys Rodolfo de Jesus
Terceiro membro da banca: FIROOZMAND , Leily Macedo
Resumo: A busca por materiais que diminuam a permeabilidade dentinária (P), tem-se tornado cada vez mais relevante devido a crescente prevalência de hipersensibilidade dentinária (HSD). O uso de biovidros pode ser uma alternativa eficaz em decorrência da bioatividade, assim como os adesivos universais, que podem ter seus efeitos otimizados quando associados ao laser de Nd:YAG, porém sua aplicação clinica carece de maiores estudos. No capítulo I objetivou-se verificar in vitro a influência do uso do laser Nd:YAG (L) associado à dois biovidros (45S5-Sílica-Si e NbG - Niobofosfato). Foram confeccionados 50 discos de dentina bovina com 6 mm de diâmetro e 1 mm de espessura. A (P) foi medida em 4 momentos: com a presença da smear layer, abertura máxima dos túbulos, após o tratamento e seguido do desafio erosivo com o auxílio do aparelho de permeabilidade (modelo câmara dividida-ODEME). Os espécimes foram randomicamente distribuídos em 5 grupos experimentais (n=10), de acordo com o tratamento realizado: (L) nos parâmetros 60mJ, 10 Hz, 0,6 W e 80mJ, 10 Hz, 0,8 W associado ao biovidro de Si (Si60 e Si80), biovidro de NbG, (NbG60 e NbG80) e Controle (C). Alguns espécimes foram selecionados para microscopia eletrônica de varredura (MEV) e espectrometria dispersiva de raio-x (EDS). Foram obtidas as variações percentuais da (P) após os diferentes tratamentos e erosão, por meio do teste Kruskal Wallis com post hoc de Dunn (p>0.05). Verificou-se que os grupos com Si apresentaram maior diminuição de (P). O 45S5 apresentou uma maior diminuição dos valores de (P) comparado aos grupos tratados com NbG, Si80 (26,12±8,16) - Si60 (42,20±9,39) > NbG80 (46,28±9,39) > NbG60 (74,63±9.68). Os tratamentos mostram-se resistentes à erosão quando comparados ao grupo (C). A análise do MEV e EDS comprovaram a formação de uma camada bioativa e todos os grupos, se mostraram resistentes ao desafio erosivo. NbG e 45S5 quando associados ao Nd:YAG (60/80mJ), apresentaram significativa redução da (P), visto que o biovidro 45S5 pareceu promover maior redução da (P) em relação ao NbG. No capítulo II objetivou verificar in vitro, por meio da (CH), a influência da associação do Adesivo universal (3M ESPE) ao (L) para a diminuição da (P). 40 discos de dentina foram confeccionados e a (P) medida da mesma forma do estudo anterior. As amostras foram randomicamente distribuídas em 4 grupos experimentais (n=10), de acordo com o tratamento realizado: A60 – Adesivo + Nd:YAG (60mJ,10Hz,0,6W), A80 – Adesivo + Nd:YAG (80mJ,10Hz,0,8 W) AU – Apenas adesivo e C–Controle (sem tratamento) e depois submetidas ao desafio erosivo. Algumas amostras foram preparadas para avaliação em (MEV) e (EDS). Os testes Kruskal Wallis e post hoc de Dunn (p>0.05) demonstraram que não houve diferença estatística entre os grupos AU, A60 e A80. Após desafio erosivo todos os tratamentos se mostraram resistentes. O uso do sistema adesivo Universal sobre a dentina, bem como a sua associação ao laser Nd:YAG (60 e 80mJ), apresentaram semelhante redução da permeabilidade dentinária e resistência ao desafio erosivo.
Abstract: The search for materials that decrease dentin permeability (P), has become increasingly relevant due to the increasing prevalence of dentin hypersensitivity (HSD). The use of bio-glasses may be an effective alternative due to bioactivity, as well as the universal adhesives, which may have their optimized effects when associated with Nd: YAG laser, but its clinical application lacks further studies. In Chapter I, the influence of the Nd: YAG (L) laser associated to the two bioglasses (45S5-Silica-Si and NbG-Niobophosphate) investigated was in vitro. Fifty discs of bovine dentin with 6 mm diameter and 1 mm thickness made.were A (P) measured was in 4 moments: with the presence of the smear layer, maximum opening of the tubules, after the treatment and followed by the erosive challenge with the aid of the permeability apparatus (divided chamber model-ODEME). The specimens were randomly distributed in 5 experimental groups (n = 10), according to the treatment performed: (L) in the parameters 60mJ, 10 Hz, 0,6 W and 80mJ, 10 Hz, 0,8 W associated to the bioglass of Si (Si60 and Si80), NbG bioglass, (NbG60 and NbG80) and Control (C). Some specimens selected were for scanning electron microscopy (SEM) and dispersive x-ray spectrometry (EDS). The percentage variations of (P) after the different treatments and erosion obtained were by Kruskal Wallis test with Dunn post hoc test (p> 0.05). It found was that the groups with Si showed a greater decrease of (P). The 45S5 showed a greater decrease of (P) values compared to the groups treated with NbG, Si80 (26.12 ± 8.16) - Si60 (42.20 ± 9.39)> NbG80 (46.28 ± 9.39)> NbG60 (74.63 ± 9.68). Treatments are resistant to erosion when compared to group (C). The SEM and EDS analysis proved the formation of a bioactive layer and all the groups showed resistance to the erosive challenge. NbG and 45S5 when associated to Nd: YAG (60 / 80mJ), showed a significant reduction of (P), since the 45S5 bioglass seemed to promote a greater reduction of (P) in relation to NbG. In Chapter II, the influence of Universal Adhesion (3M ESPE) to (L) for the decrease of (P) was investigated in vitro. 40 dentin disks were made and (P) measured in the same way as the previous study. A60 - Adhesive + Nd: YAG (60mJ, 10Hz, 0.6W), A80 - Adhesive + Nd: YAG (80mJ, 10Hz) were randomly distributed in 4 experimental groups (n = 10) , 0.8 W) AU - Adhesive only and C-Control (without treatment) and then submitted to the erosive challenge. Some samples were prepared for evaluation in (SEM) and (EDS). Kruskal Wallis and Dunn's post hoc tests (p> 0.05) showed that there was no statistical difference between the AU, A60 and A80 groups. After erosive challenge, all treatments were resistant. The use of the Universal adhesive system on the dentin, as well as its association with Nd: YAG laser (60 and 80mJ), presented similar reduction of dentin permeability and resistance to erosive challenge.
Palavras-chave: Sensibilidade da dentina; Permeabilidade da dentina; Lasers; Adesivos dentinários; Biovidros.
Dentin sensitivity; Permeability of dentin; Lasers; Adhesives; Bioglass.
Área(s) do CNPq: Odontologia
Idioma: por
País: Brasil
Instituição: Universidade Federal do Maranhão
Sigla da instituição: UFMA
Departamento: DEPARTAMENTO DE ODONTOLOGIA I/CCBS
Programa: PROGRAMA DE PÓS-GRADUAÇÃO EM ODONTOLOGIA/CCBS
Citação: PENHA, Karla Janilee De Souza. Análise da permeabilidade dentinária após irradiação com o laser de nd:yag associado a adesivo universal e diferentes biovidros. 2018. 93 p. Dissertação (Programa de Pós-Graduação em Odontologia/CCBS) - Universidade Federal do Maranhão, São Luís.
Tipo de acesso: Acesso Aberto
URI: https://tedebc.ufma.br/jspui/handle/tede/tede/2262
Data de defesa: 16-Dec-2016
Appears in Collections:DISSERTAÇÃO DE MESTRADO - PROGRAMA DE PÓS-GRADUAÇÃO EM ODONTOLOGIA

Files in This Item:
File Description SizeFormat 
KarlaPenha.pdfDissertação de Mestrado5,35 MBAdobe PDFDownload/Open Preview


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.