Título: PREPARAÇÃO DE UM MATERIAL DE REFERÊNCIA IN HOUSE PARA Fe, Ca, Si, Ni, Na, P E V EM ELETRODOS DE CARBONO DA INDÚSTRIA DE ALUMÍNIO
Título(s) alternativo(s): PREPARATION OF A REFERENCE MATERIAL "IN HOUSE" FOR Fe, Ca, Si, Ni, Na, P AND V IN CARBON ELECTRODES OF THE ALUMINUM INDUSTRY
Autor: Silva, Marcos Moura 
Primeiro orientador: SANTANA, Sirlane Aparecida Abreu
Resumo: O uso de materiais de referências certificados é uma alternativa que os laboratórios têm para garantir a qualidade de suas análises, razão pela qual muitos deles vêm investindo na produção de seus próprios materiais de referências in-house. Este trabalho apresenta aplicação de um ensaio interlaboratorial na certificação de Fe, Ca, Si, Ni, Na, P e V em uma amostra de eletrodos de carbono, candidata a material de referência in-house, de uma indústria de alumínio no Brasil. Amostras britadas, moídas e quarteadas foram envasadas em 128 frascos. Testes de homogeneidade e estabilidade atestaram que o material manteve-se homogêneo após o envase e estável na sua composição ao longo do tempo de estudo. A certificação do material se deu através de um programa de interlaboratorial que contou com a participação de sete laboratórios em diferentes locais. Após a aplicação dos testes de Cochran e Grubbs aos valores fornecidos pelos laboratórios, os valores certificados em ppm foram: 589,08 ± 25,28 para Fe; 142,89 ± 12,03 para Ca; 332,03 ± 20,55 para V; 178,07 ± 9,26 para Ni; 326,11 ± 24,07 para Na; 134,17 ± 6,59 para Si e 7,38 ± 1,97 para o P. Por fim, os laboratórios foram comparados por meio do teste z-score e observou-se desempenho satisfatório, exceto para o laboratório 1, nas análises de Si, que apresentou desvio discrepante dos demais A aplicação da análise de variâncias aos valores reportados levou a conclusão de que o material era homogêneo e estável o suficiente para ser usado como um material de referência para controle de qualidade interno.
Abstract: The use of certified reference materials is an alternative that laboratories have to ensure the quality of their analyzes. Many laboratories have been investing in the production of their own reference materials in-house. This study presents the application of an interlaboratory test on the certification of Fe, Ca, Si, Ni, Na, P and V in a sample of carbon electrodes candidate reference material in-house, from an aluminum industry in Brazil. The sample was crushed, milled and quartered. Subsequently, the material was filled into 128 botlles. Homogeneity tests were conducted on material that testified that the material remained homogeneous after preparation and stable over time of study. The material certification was made through a collaborative program which included the participation of seven laboratories in different locations. After applying the Cochran and Grubbs tests the values provided by laboratories certified values in ppm were: 589.08 ± 25.28 for Fe, 142.89 ± 12.03 for Ca; 332.03 ± 20.55 to V, 178.07 ± 9.26 for Ni, 326.11 ± 24.07 for Na; 134.17 ± 6.59 for Si and 7.38 ± 1.97 for P. Finally, the laboratories were compared using the z-score test and was observed satisfactory performance, except for the the laboratory 1 for Si analysis, which showed discrepant deviation of the others. The application of variance analysis led to the conclusion that the material was homogeneous and stable enough to be used as a reference material for quality control procedure.
Palavras-chave: Materiais de referência
Certificação interlaboratorial
Material carbonáceo
Reference materials
Interlaboratory certification
Carbonaceous material
Área(s) do CNPq: CNPQ::CIENCIAS EXATAS E DA TERRA::QUIMICA::QUIMICA ANALITICA
Idioma: por
País: BR
Instituição: Universidade Federal do Maranhão
Sigla da instituição: UFMA
Departamento: QUIMICA
Programa: PROGRAMA DE PÓS-GRADUAÇÃO EM QUÍMICA/CCET
Citação: SILVA, Marcos Moura. PREPARATION OF A REFERENCE MATERIAL "IN HOUSE" FOR Fe, Ca, Si, Ni, Na, P AND V IN CARBON ELECTRODES OF THE ALUMINUM INDUSTRY. 2014. 80 f. Dissertação (Mestrado em QUIMICA) - Universidade Federal do Maranhão, São Luís, 2014.
Tipo de acesso: Acesso Aberto
URI: http://tedebc.ufma.br:8080/jspui/handle/tede/988
Data de defesa: 28-Mar-2014
Aparece nas coleções:DISSERTAÇÃO DE MESTRADO - PROGRAMA DE PÓS-GRADUAÇÃO EM QUIMICA

Arquivos associados a este item:
Arquivo TamanhoFormato 
Dissertacao MARCOS MOURA SILVA.pdf1,13 MBAdobe PDFBaixar/Abrir Pré-Visualizar


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.