Exportar este item: EndNote BibTex

Use este identificador para citar ou linkar para este item: https://tedebc.ufma.br/jspui/handle/tede/tede/1939
Registro completo de metadados
Campo DCValorIdioma
dc.creatorALVES, Luana Cristina Feitosa-
dc.creator.Latteshttp://lattes.cnpq.br/2599661679596299por
dc.contributor.advisor1PEDROCHI, Franciana-
dc.contributor.advisor1Latteshttp://lattes.cnpq.br/7034087210537720por
dc.contributor.advisor-co1STEIMACHER, Alysson-
dc.contributor.advisor-co1Latteshttp://lattes.cnpq.br/7599331855053094por
dc.contributor.referee1SATO, Francielle-
dc.contributor.referee1Latteshttp://lattes.cnpq.br/7314370428188000por
dc.contributor.referee2WEINAND, Wilson Ricardo-
dc.contributor.referee2Latteshttp://lattes.cnpq.br/2603073361974513por
dc.contributor.referee3BARBOSA, Marcio José-
dc.contributor.referee3Latteshttp://lattes.cnpq.br/8966700125639095por
dc.date.accessioned2017-09-21T17:41:19Z-
dc.date.issued2017-07-13-
dc.identifier.citationALVES, Luana Cristina Feitosa. Estudo da influência do fluoreto de cálcio na bioatividade de vidros borato. 2017. 69 f. Dissertação (Mestrado em Ciência dos Materiais) - Universidade Federal do Maranhão, Imperatriz, 2017.por
dc.identifier.urihttps://tedebc.ufma.br/jspui/handle/tede/tede/1939-
dc.description.resumoVidros boratos bioativos têm apresentado resultados superiores aos vidros silicatos bioativos, quando comparamos suas taxas de conversão em apatita e seu potencial de bioatividade. Neste trabalho sintetizamos novos vidros boratos com a composição básica 60B2O3 - 4P2O5 - 18Na2O – xCaF2 – (18-xCaO), com x = 0, 5 e 10 % em massa, e investigamos a influência da adição de CaF2 na bioatividade das amostras in vitro, em um período de 28 dias, em um simulador do fluído corporal (SBF). As medidas de DRX, antes da imersão, apresentaram bandas largas, comprovando a estrutura amorfa dos vidros. E verificou-se por meio das análises de Densidade, análise térmica, DRX, Raman e FTIR, que a adição de CaF2 até 10%, em massa, não provocou grandes mudanças estruturais na amostras. Por meio da calorimetria exploratória diferencial, determinamos a estabilidade térmica dos vidros que apresentaram valores acima de 120°C. A bioatividade foi investigada por meio das técnicas de difração de raios-X (DRX), espectroscopia Raman e FTIR, e pela medida do pH da solução SBF. Os resultados obtidos mostraram que, em 24h, houve um aumento no pH da solução SBF, o que contribui para a dissolução da camada mais externa do vidro e sua conversão em apatita. Nos difratogramas (DRX) para as amostras imersas por 7 dias, houve a formação de picos cristalinos, em 26° e 32° (2ϴ), em todas as amostras medidas. Esses picos correspondem aos padrões de hidroxiapatita. A presença de CaF2 na composição das amostras imersas por 7 dias apresentou picos em 28° (2ϴ) correspondendo a fluorapatita. A intensidade destes picos apresentou um aumento em função do tempo de imersão, durante todo período estudado. As medidas de Raman confirmaram os resultados do DRX, apresentando para todas as amostras espectros característicos da hidroxiapatita em 960 cm-1 . As amostras preparadas com CaF2 apresentaram picos em 965 cm-1 , que corresponde a fluorapatita. O FTIR confirmou os resultados apresentados no DRX e Raman, em que todas as amostras apresentaram um pico centrado em 1041 cm-1 para a hidroxiapatita e 1042 cm-1 característico para a fluorapatita. Os resultados demonstram que as amostras preparadas apresentam potencial para serem usados como biomateriais em aplicações biomédicas, como ortopedia, odontologia e engenharia de tecidos.por
dc.description.abstractBioactive borate glass has presented superior results then bioactive silicate glasses, when compared its conversion rates in apatite and its potential of bioactivity. In this work, new Borate glasses with the basic 60B2O3 - 4P2O5 - 18Na2O – xCaF2 – (18-xCaO), com x = 0, 5 e 10 % wt were synthesized, and investigated the influence of CaF2 addition on bioactivity of samples in vitro, in a period of 28 days in a simulator of the body fluid (SBF). This bioactivity was investigated by means of X-ray diffraction (DRX), Raman Spectroscopy, FTIR and by the measure of pH. DRX measures, prior to immersion, presented wide bands, evidencing the amorphous structure of glasses. The results of density, thermal analysis, XRD, Raman and FTIR show that the addition of CaF2, until 10 % wt, did not cause significant changes in samples network structure. The thermal stability for all samples was calculated from DSC data and all presented values up to 120°C. The results of pH of SBF solution show increase from for 24 hours, which contributes to the dissolution of the outermost layer of the glass and the precipitation of apatite. In XRD data for 60B sample soaked in SBF for 7 days, there was formation of crystalline peaks, at 26° and 32° (2ϴ), in all measures. These peaks correspond to patterns of hydroxyapatite (HA). The XRD spectra in 60B5CaF and 60B10CaF, soaked in SBF for 7 days, presented peaks in 28°(2ϴ) corresponding to fluorapatite (FA), due to the presence of CaF2 in these glasses. Raman and FTIR measurements confirmed what was measured by XRD, showing characteristic peaks of HA and FA for all the samples. Results show that the prepared samples present potential for being used as biomaterials in biomedical applications, such as orthopedics, dentistry and tissue engineering.eng
dc.description.provenanceSubmitted by Rosivalda Pereira (mrs.pereira@ufma.br) on 2017-09-21T17:41:19Z No. of bitstreams: 1 LuanaAlves.pdf: 1633592 bytes, checksum: 785a3f9aa7f3fc08d80023603f457b39 (MD5)eng
dc.description.provenanceMade available in DSpace on 2017-09-21T17:41:19Z (GMT). No. of bitstreams: 1 LuanaAlves.pdf: 1633592 bytes, checksum: 785a3f9aa7f3fc08d80023603f457b39 (MD5) Previous issue date: 2017-07-13eng
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superiorpor
dc.description.sponsorshipConselho Nacional de Desenvolvimento Científico e Tecnológicopor
dc.description.sponsorshipFundação de Amparo à Pesquisa e ao Desenvolvimento Científico e Tecnológico do Maranhãopor
dc.formatapplication/pdf*
dc.languageporpor
dc.publisherUniversidade Federal do Maranhãopor
dc.publisher.departmentCOORDENAÇÃO DO CURSO DE CIÊNCIA E TECNOLOGIA - IMPERATRIZ/CCSSTpor
dc.publisher.countryBrasilpor
dc.publisher.initialsUFMApor
dc.publisher.programPROGRAMA DE PÓS-GRADUAÇÃO EM CIÊNCIA DOS MATERIAIS/CCSSTpor
dc.rightsAcesso Abertopor
dc.subjectVidros boratos bioativospor
dc.subjectBioatividadepor
dc.subjectHidroxiapatitapor
dc.subjectFluorapatitapor
dc.subjectBiomateriaispor
dc.subjectSimulator of the body fluidpor
dc.subjectBioactive borate glasspor
dc.subjectBioactivitypor
dc.subjectHydroxyapatite;por
dc.subjectFluorapatitepor
dc.subjectBiomaterialpor
dc.subject.cnpqFísica da Matéria Condensadapor
dc.titleEstudo da influência do fluoreto de cálcio na bioatividade de vidros boratopor
dc.title.alternativeStudy of the influence of calcium fluoride on the bioactivity of borate glasseseng
dc.typeDissertaçãopor
Aparece nas coleções:DISSERTAÇÃO DE MESTRADO - PROGRAMA DE PÓS-GRADUAÇÃO EM CIÊNCIA DOS MATERIAIS/CCSST

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
LuanaAlves.pdfDissertação1,6 MBAdobe PDFBaixar/Abrir Pré-Visualizar


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.