Título: Efeito do jateamento com vidro niobofosfato na resistência de união de um adesivo em dentina afetada por cárie
Título(s) alternativo(s): Effect of blasting with niobophosphate glass on the bond strength of an adhesive in dentin affected by caries
Autor: Leal, Adriana Mara Araújo 
Primeiro orientador: BAUER, José Roberto de Oliveira
Resumo: Objetivo: Avaliar o efeito do jateamento de micropartículas de vidro niobofosfato (NbG) na resistência de união (RU) e na longevidade de um sistema adesivo em diferentes substratos dentinários. Dezoito molares extraídos livres de cárie foram usados. As superfícies de dentina foram avaliadas em três grupos: (1) Controle – Dentina Sadia; (2) Remoção parcial do tecido cariado; (3) Remoção total do tecido cariado. Metade dos dentes de cada grupo sofreu um jateamento com partículas de NbG (15s/1cm/5bar). Em seguida o adesivo Clearfil S3 Bond Plus foi aplicado e uma coroa de resina composta foi construída. Os dentes foram seccionados para obtenção dos espécimes (1,0 mm2) e submetidos ao teste de microtração (0,5 mm/min) imediatamente e após 6 meses de estocagem em água. Os padrões de fratura foram avaliados usando estereomicroscópio (40x) e levados ao microscópio eletrônico de varredura (SEM). Os dados foram analisados pelos testes Kruskal-Wallis (pos-hoc Dunn) e Mann-Whitney (α=0.05). Resultados: A dentina sadia apresentou os maiores valores de RU. O jateamento com NbG aumentou os valores de RU no grupo remoção total. Os valores de RU no período de 24h foram superiores ao de 6 meses. A maioria das fraturas dos espécimes foi adesiva/mista. Conclusão: Os autores concluíram que o jateamento à dentina com partículas NbG aumentou a RU no grupo onde a dentina cariada foi totalmente removida.
Abstract: Objectives: To evaluate the effect of airborne-particle abrasion with niobium phosphate bioglass (NbG) microparticles on the bond strength (µTBS) and longevity of an adhesive system to different dentin substrates. Methods and Materials: Caries-free molars were used in this study. The dentin surfaces were evaluated in three groups: (1) Control – Healthy Dentin; (2) Partial removal of carious tissue; (3) complete removal of carious tissue. Half the teeth in each group were submitted to airborne-particle abrasion with NbG microparticles (15s/1cm/5bar). After this, the adhesive Clearfil S3 was applied and composite buildups were constructed incrementally; and specimens were longitudinally sectioned to obtain bonded sticks (1.0 mm2) to be tested in tension (0.5 mm/min) immediately or after 6 months of storage in water. The fracture patterns were evaluated by stereomicroscope (40x) and then by scanning electron microscopy (SEM). The data were analyzed by the Kruskal-Wallis (post-hoc Dunn) and Mann-Whitney tests (α=0.05). Results: Healthy dentin showed the highest bond strength (µTBS). Airborne-particle abrasion with NbG increased the µTBS values in the complete caries removal group. The bond strength values in the 24-hr period were higher than those at 6 months. In the majority of the specimens the fracture mode was adhesive/ mixed. Conclusion: The authors concluded that airborne-particle abrasion on dentin with NbG particles increased the µTBS in the group in which carious dentin was completely removed.
Palavras-chave: Dentina afetada por cárie
Adesivo autocondicionante
Microtração
Vidro bioativo
Caries-affected dentin
Self-etching adhesive
Microtensile
Bioactive glass
Área(s) do CNPq: Odontologia
Materiais Odontológicos
Idioma: por
País: Brasil
Instituição: Universidade Federal do Maranhão
Sigla da instituição: UFMA
Departamento: DEPARTAMENTO DE ODONTOLOGIA I/CCBS
Programa: PROGRAMA DE PÓS-GRADUAÇÃO EM ODONTOLOGIA/CCBS
Citação: LEAL, Adriana Mara Araújo. Efeito do jateamento com vidro niobofosfato na resistência de união de um adesivo em dentina afetada por cárie. 2016. 69 f. Tese (Programa de Pós-Graduação em Odontologia) - Universidade Federal do Maranhão, São Luís, 2016.
Tipo de acesso: Acesso Aberto
URI: http://tedebc.ufma.br:8080/jspui/handle/tede/1369
Data de defesa: 29-Fev-2016
Aparece nas coleções:TESE DE DOUTORADO - PROGRAMA DE PÓS-GRADUAÇÃO EM ODONTOLOGIA

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
AdrianaLeal.pdfTese1,57 MBAdobe PDFBaixar/Abrir Pré-Visualizar


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.