Título: Estudo estrutural, térmico e vibracional do crista de Bis (L-alaninato) de Níquel (II) di-hidratado
Título(s) alternativo(s): STRUCTURAL, THERMAL AND VIBRATIONAL STUDY OF BIS (L-ALANINATE) CRYSTAL OF NICKEL (II) DIHYDRATE
Autor: Baldez, Thays Silva 
Primeiro orientador: MENEZES, Alan Silva de
Primeiro coorientador: Santos, Adenilson Oliveira dos
Resumo: Aminoácidos complexados com metais de transição têm atraído cada vez mais o interesse de pesquisadores devido à grande variedade de propriedades físicas que eles apresentam para o entendimento das interações metal-aminoácido. Neste trabalho, cristais de Bis(L-alaninato) de Níquel (II) di-hidratado [Ni(C3H6O2N)2(H2O)2.2H2O] foram obtidos por meio da evaporação lenta do solvente de uma solução saturada contendo 0,1 mol/L de NiCl2.6H2O, 0,2 mol/L de L-alanina e NaOH. Após a obtenção da amostra, a confirmação da estrutura deu-se por refinamento de Rietveld. As propriedades estruturais desses cristais foram estudadas por medidas de difração de raios-X em função da temperatura na faixa de 25 a 150 °C. Experimentos de análise térmica foram realizados por TG/DTA entre 25 e 500 °C e por DSC entre 25 e 250 °C. Os resultados obtidos por TG/DTA evidenciam a saída das moléculas de água do cristal de Bis(L-alaninato) de Níquel (II) di-hidratado nas temperaturas de 64,51 e 117,25 °C, que também foi confirmada pelos resultados obtidos por DSC. O padrão de difração de raios-X mostrou desaparecimento e o surgimento de novos picos no difratograma, para temperaturas próximas a 55 °C e 110 °C, indicando a saída de água do cristal. Essa transformação é irreversível, pois o padrão de difração obtido após a amostra retornar à temperatura ambiente difere significativamente daquele obtido antes do aquecimento. As propriedades vibracionais foram analisadas por Espectroscopia Raman entre 25 e 185 °C. As medidas dos espectros Raman em função da temperatura evidenciam a saída das moléculas de água. O espectro à alta temperatura se assemelha ao espectro à temperatura ambiente, mostrando que o cristal sofre transformação de fase, mas provavelmente permanece com a mesma simetria cristalina.
Abstract: Amino acids complex of transition metals has increasingly attracted the interest of researchers due to their wide range of physical properties for understanding metal-amino acid interactions. In this work [Bis(L-Alaninato)Diaqua] Nickel(II) Dihydrate [Ni(C3H6O2N)2(H2O)2.2H2O] crystals were obtained by slow evaporation method using 0,1 mol/L of NiCl2.6H2O, 0,2 mol/L of L-alanine and NaOH. Rietveld refinement of X-ray data confirmed the structure. The structural properties of these crystals were studied by X-ray diffraction (XRD) in the temperature range from 25 to 150 °C. Thermal analysis experiments were performed by TG/DTA between 25 and 500 °C, and by DSC between 25 and 250 °C. The results obtained by TG/DTA indicate the loss of water molecules by [Bis(L-Alaninato)Diaqua] Nickel(II) Dihydrate crystals at temperatures of 64 and 117 °C, which was also confirmed by the results obtained by DSC. The X-ray diffraction pattern show new peaks, in temperatures around 55 and 110 ° C, indicating to loss of water by crystals. The transformation is irreversible because the diffraction pattern obtained after the sample return to the room temperature differs from that obtained before heating of the sample. The vibrational properties were analyzed by Raman spectroscopy between 25 and 185 °C. The Raman spectroscopy measurements as a function of the temperature show the loss of water molecules. The spectra at high temperatures resemble the spectrum at room temperature, showing that the crystal undergoes phase transformation, but probably do not change the crystal symmetry.
Palavras-chave: Complexo de aminoácido
Difração de raios-X
Espectroscopia Raman
Estabilidade térmica
Amino acid complex
X-ray diffraction
Raman spectroscopy
Thermal stability
Área(s) do CNPq: Física da Matéria Condensada
Idioma: por
País: Brasil
Instituição: Universidade Federal do Maranhão
Sigla da instituição: UFMA
Departamento: COORDENAÇÃO DO CURSO DE CIENCIA E TECNOLOGIA - IMPERATRIZ/CCSST
Programa: PROGRAMA DE PÓS-GRADUAÇÃO EM CIÊNCIA DOS MATERIAIS/CCSST
Citação: BALDEZ, Thays Silva. Estudo estrutural, térmico e vibracional do crista de Bis (L-alaninato) de Níquel (II) di-hidratado. 2016. 80 f. Dissertação (Programa de Pós-Graduação em Ciência dos Materiais) - Universidade Federal do Maranhão, Imperatriz, 2016 .
Tipo de acesso: Acesso Aberto
URI: http://tedebc.ufma.br:8080/jspui/handle/tede/1344
Data de defesa: 6-Jul-2016
Appears in Collections:DISSERTAÇÃO DE MESTRADO - PROGRAMA DE PÓS-GRADUAÇÃO EM CIÊNCIA DOS MATERIAIS/CCSST

Files in This Item:
File Description SizeFormat 
ThaysSilvaBaldez.pdfDissertação2,05 MBAdobe PDFDownload/Open Preview


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.